Abstract High-entropy alloys (HEAs) with multiple principal elements represent a paradigm shift in structural alloy design and show excellent surface degradation resistance in corrosive environment. Here, the tribo-corrosion response of laser-engineered net-shaped CoCrFeMnNi HEA was evaluated in 3.5 wt% NaCl solution at room temperature. The additively manufactured (AM-ed) CoCrFeMnNi showed five times lower wear rate, regenerative passivation, and nobler corrosion potential during tribo-corrosion test compared to its arc-melted counterpart. A significant anisotropy was seen in the tribo-corrosion response with 45° to the build direction showing better performance compared to tests along the build direction and perpendicular to it. The open circuit potential curves were characterized by a sharp drop to more negative values as wear began, followed by continuous change for the active tribo-corrosion duration and finally a jump to nobler value at the end of the test indicating excellent surface re-passivation for the AM-ed alloy. The superior tribo-corrosion resistance of AM-ed CoCrFeMnNi was attributed to the refined microstructure and highly protective surface passivation layer promoted by the sub-grain cellular structure formed during additive manufacturing. These results highlight the potential of utilizing additive manufacturing of HEAs for use in extreme environments that require a combination of tribo-corrosion resistance, mechanical durability, extended service life, and net shaping with low dimensional tolerance. 

There is a strong demand for materials with inherently high creep resistance in the harsh environment of next-generation nuclear reactors. High entropy alloys have drawn intense attention in this regard due to their excellent elevated temperature properties and irradiation resistance. Here, the time-dependent plastic deformation behavior of two refractory high entropy alloys was investigated, namely HfTaTiVZr and TaTiVWZr. These alloys are based on reduced activity metals from the 4-5-6 elemental palette that would allow easy post-service recycling after use in nuclear reactors. The creep behavior was investigated using nano-indentation over the temperature range of 298 K to 573 K under static and dynamic loads up to 5 N. Creep stress exponent for HfTaTiVZr and TaTiVWZr was found to be in the range of 20–140 and the activation volume was ~16–20b3, indicating dislocation dominated mechanism. The stress exponent increased with increasing indentation depth due to a higher density of dislocations and their entanglement at larger depth and the exponent decreased with increasing temperature due to thermally activated dislocations. Smaller creep displacement and higher activation energy for the two high entropy alloys indicate superior creep resistance compared to refractory pure metals like tungsten.